Bahan Kabel Penebat Bersinar Halogen Sifar Asap Rendah (Bahan Kabel Penebat Bersinar LSZH)
CIRI-CIRI PRODUK
SKOP PENGGUNAAN
![](https://ecdn6.globalso.com/upload/p/188/image_other/2023-11/6549a00c44c3f87882.jpg)
![](https://ecdn6.globalso.com/upload/p/188/image_other/2023-11/65499ffe10fb494896.jpg)
![](https://ecdn6.globalso.com/upload/p/188/image_other/2023-11/6549a0148f8d034204.jpg)
![](https://ecdn6.globalso.com/upload/p/188/image_other/2023-11/6549a01d5f35215664.jpg)
Item dan piawaian ujian
Item pemeriksaan | Unit | Rkeperluan | |||
WDZ-Y-J70 | WDZ-Y-H70 | WDZ-Y-H90 | |||
1 | Kekuatan tegangan | MPa | ≥10. 0 | ≥10. 0 | ≥10. 0 |
2 | Pemanjangan pada waktu rehat | % | ≥160 | ≥160 | ≥160 |
3 | Ruang penuaan udara |
|
|
|
|
Suhu penuaan | ℃ | 100±2 | 100±2 | 110±2 | |
Masa penuaan | h | 168 | 168 | 240 | |
Kadar perubahan maksimum kekuatan tegangan | % | ±25 | ±25 | ±25 | |
Kadar maksimum perubahan pemanjangan semasa putus | % | ±25 | ±25 | ±25 | |
4 | Ubah bentuk terma |
|
|
|
|
Ujian suhu | ℃ | 90±2 | 90±2 | 90±2 | |
Hasil eksperimen | % | ≤50 | ≤50 | ≤50 | |
5 | 20 ℃ kerintangan isipadu | Oh · m | ≥1. 0×1012 | ≥1. 0×1010 | ≥1. 0×1010 |
6 | Kerintangan isipadu pada suhu operasi |
|
|
|
|
Ujian suhu | ℃ | 70±1 | — | — | |
Kerintangan isipadu | Oh · m | ≥2. 0×108 | — | — | |
7 | Kekuatan dielektrik | MV/m | ≥20 | ≥18 | ≥18 |
8 | Ujian kejutan haba |
|
|
|
|
Ujian suhu | ℃ | 130±3 | 130±3 | 130±3 | |
Masa ujian | % | 1 | 1 | 1 | |
Hasil eksperimen | — | Tiada keretakan | Tiada keretakan | Tiada keretakan | |
9 | Kesan suhu kerapuhan |
|
|
|
|
Ujian suhu | ℃ | -25 | -25 | -25 | |
Hasil eksperimen | Nombor | ≤15/30 | ≤15/30 | ≤15/30 | |
10 | Ujian rintangan ozon |
|
|
|
|
Ujian suhu | ℃ | — | 25±2 | 25±2 | |
masa percubaan | h | — | dua puluh empat | dua puluh empat | |
Kepekatan ozon | ppm | — | 250~300 | 250~300 | |
Hasil eksperimen | — | — | Tiada keretakan | Tiada keretakan | |
11 | Ujian rendaman air panas |
|
|
|
|
Ujian suhu | ℃ | — | 70±2 | 70±2 | |
masa percubaan | h | — | 168 | 168 | |
Kadar perubahan maksimum kekuatan tegangan | % | — | ±30 | ±30 | |
Kadar maksimum perubahan pemanjangan semasa putus | % | — | ±35 | ±35 | |
12 | Indeks oksigen | % | ≥28 | ≥30 | ≥30 |
13 | Ketumpatan asap |
|
|
|
|
tanpa api | — | ≤350 | ≤350 | ≤350 | |
menyala | — | ≤100 | ≤100 | ≤100 | |
14 | Pembakaran membebaskan keasidan gas |
|
|
|
|
Kandungan HCI dan HBr | % | ≤0.5 | ≤0.5 | ≤0.5 | |
kandungan HF | % | ≤0.1 | ≤0.1 | ≤0.1 | |
nilai pH | — | ≥4.3 | ≥4.3 | ≥4.3 | |
Kekonduksian elektrik | μS/mm | ≤10 | ≤10 | ≤10 | |
15 | Bahaya ketoksikan asap bahan | Mengikut keperluan aplikasi produk, dirundingkan oleh pihak penawaran dan permintaan. |