English French German Portuguese Spanish Russian Japanese Korean Arabic Irish Greek Turkish Italian Danish Romanian Indonesian Czech Afrikaans Swedish Polish Basque Catalan Esperanto Hindi Lao Albanian Amharic Armenian Azerbaijani Belarusian Bengali Bosnian Bulgarian Cebuano Chichewa Corsican Croatian Dutch Estonian Filipino Finnish Frisian Galician Georgian Gujarati Haitian Hausa Hawaiian Hebrew Hmong Hungarian Icelandic Igbo Javanese Kannada Kazakh Khmer Kurdish Kyrgyz Latin Latvian Lithuanian Luxembou.. Macedonian Malagasy Malay Malayalam Maltese Maori Marathi Mongolian Burmese Nepali Norwegian Pashto Persian Punjabi Serbian Sesotho Sinhala Slovak Slovenian Somali Samoan Scots Gaelic Shona Sindhi Sundanese Swahili Tajik Tamil Telugu Thai Ukrainian Urdu Uzbek Vietnamese Welsh Xhosa Yiddish Yoruba Zulu Kinyarwanda Tatar Oriya Turkmen Uyghur
Leave Your Message
Bahan Kabel Bertebat Polivinil Klorida (Bahan Kabel Bertebat PVC)
Kategori Produk
Produk Pilihan
0102
Bahan Kabel Bertebat Polivinil Klorida (Bahan Kabel Bertebat PVC)
Bahan Kabel Bertebat Polivinil Klorida (Bahan Kabel Bertebat PVC)
Bahan Kabel Bertebat Polivinil Klorida (Bahan Kabel Bertebat PVC)

Bahan Kabel Bertebat Polivinil Klorida (Bahan Kabel Bertebat PVC)

1. Ia mempunyai sifat dielektrik yang sangat baik, rintangan kakisan yang kuat, kekuatan mekanikal, kebolehkitar semula dan ciri-ciri lain.

2. Bahan kabel bertebat PVC digunakan secara meluas dalam kehidupan seharian, dan teknologi pembuatannya matang, mudah dibentuk dan diproses. Berbanding dengan jenis bahan penebat kabel yang lain, ia bukan sahaja kos rendah, tetapi juga boleh dikawal dengan berkesan dari segi perbezaan warna, kemasan matte, percetakan, kecekapan pemprosesan, kelembutan dan kekerasan, lekatan konduktor, sifat mekanikal dan fizikal dan sifat elektrik wayar itu sendiri.

    Hubungi Kami
    Maklumat produk
    Tag Produk

    CIRI-CIRI PRODUK

    1. Ciri-ciri dielektrik yang sangat baik: PVC adalah bahan penebat elektrik yang baik, boleh menghalang kebocoran semasa dengan berkesan, untuk memastikan operasi sistem kabel yang selamat dan stabil.
    2. Rintangan kakisan yang kuat: Bahan kabel bertebat PVC mempunyai rintangan kakisan yang kuat terhadap banyak bahan kimia dan faktor persekitaran, supaya ia dapat mengekalkan hayat perkhidmatan yang panjang dalam pelbagai aplikasi.
    3. Kekuatan mekanikal: Bahan kabel PVC mempunyai kekuatan mekanikal yang mencukupi dan boleh menahan tegangan, penyemperitan dan tegasan lentur.
    4. Kebolehkitar semula: Bahan kabel PVC boleh dikitar semula dan digunakan semula, membantu mengurangkan kesan alam sekitar.

    SKOP PENGGUNAAN

    Kabel dan kabel optik, kabel sepaksi, kabel rangkaian, kabel lif, dsb.
    Polivinil Klorida Bertebat
    Polivinil Klorida Bertebat
    Polivinil Klorida Bertebat
    Polivinil Klorida Bertebat

    Item dan piawaian ujian

    Sifat mekanikal, fizikal dan elektrik bahan kabel polivinil klorida

    sayadia ada

     

    J-70

    JR-70

    JGD-70

    J-90

    Kekuatan tegangan/MPa              

    ≥

    15.0

    15.0

    16.0

    16.0

    Regangan tegangan semasa putus/%          

    ≥

    150

    180

    150

    150

    Ubah bentuk terma          

    ≥

    40

    50

    30

    30

    Harta rapuh tialah suhu/℃

     

    -15

    -20

    -15

    -15

    Kesan sifat kerosakkan

     

    lulus

    lulus

    lulus

    lulus

    Masa kestabilan terma pada 200℃/min 

    ≥

    60

    60

    100

    180

    Kerintangan isipadu pada 20℃/Ω·m

    ≥

    1.0×10 12

    1.0×10 11

    3.0×1012

    1.0×10 12

    Kekuatan dielektrik/(MV/m)       

    ≥

    20

    20

    25

    20

    Faktor kehilangan dielektrik(50Hz)       

    ≤

    —

    —

    0.1

    —

    Ujian suhu/℃

     

    70±1

    70±1

    70±1

    95±1

    Kerintangan isipadu/Ω·m       

    ≥

    1.0×10 9

    1.0×108

    5.0×109

    5.0×108

    Sifat mekanikal dan fizikal bahan kabel polivinil klorida selepas penuaan

    sayadia ada

     

    J-70

    JR-70

    JGD-70

    J-90

    Ujian suhu/℃

     

    100±2

    100±2

    100±2

    135±2

    Ujian masa/j

     

    168

    168

    168

    240

    Kekuatan tegangan selepas penuaan /MPa

    ≥

    15.0

    15.0

    16.0

    16.0

    Kadar perubahan kekuatan tegangan maksimum/%

     

    ±20

    ±20

    ±20

    ±20

    Regangan tegangan pada patah selepas penuaan/%

    ≥

    150

    180

    150

    150

    Kadar perubahan maksimum tegangan

    terikan semasa putus/%

     

    ±20

    ±20

    ±20

    ±20

    Keadaan ujian

     

    100±2 ℃

    100±2 ℃

    100±2 ℃

    115±2℃

     

     

    168 jam

    168 jam

    168 jam

    240 jam

    Kehilangan jisim/(g/m2)

    ≤

    20

    20

    20

    20